Figure 3
The effect of density on the stress profile τoct. ( Figure 2 loading conditions)
(a) 7.8 g cm-3, E = 207 GPa, ν = 0.30,
(b) 7.5 g cm-3, E = 175 GPa, ν = 0.28,
(c) 7.0 g cm-3, E = 140 GPa, ν = 0.27.
SEARCH
RESOURCES
INDUSTRY NEWS
- Annual Aerospace & Defense National SEA Awards select Perry Technology as Sem...
- New Centrifuge Recycling System from ALMCO...
- Boeing Recognized as NASA’s Large Business Contractor of the Year...
- Schafer Gear Adds Two to Rockford Team...
- IEMCA Partners with York Technical College...
- Gas-Fired Belt Conveyor Oven from Grieve...
- Kitamura Machining Centers Ideal for Lights-Out Manufacturing...
- Preco Names New Head of Metals Market...
- New Regional Sales Manager at Worldwide Superabrasives...
- Wasino Becomes Amada Wasino America, Inc....
- ZPS America Formed to Market Multispindle CNC Machines...
- New Director of Global Sales at Sunnen...
stkplFig3_1006
Figure 3
The effect of density on the stress profile τoct. ( Figure 2 loading conditions)
(a) 7.8 g cm-3, E = 207 GPa, ν = 0.30,
(b) 7.5 g cm-3, E = 175 GPa, ν = 0.28,
(c) 7.0 g cm-3, E = 140 GPa, ν = 0.27.
Figure 3
The effect of density on the stress profile τoct. ( Figure 2 loading conditions)
(a) 7.8 g cm-3, E = 207 GPa, ν = 0.30,
(b) 7.5 g cm-3, E = 175 GPa, ν = 0.28,
(c) 7.0 g cm-3, E = 140 GPa, ν = 0.27.